Radioluminescence of silver halide optical fibers

Yoram Kirsh, I. Schnitzer, P. Townsend

פרסום מחקרי: פרסום בכתב עתמאמרביקורת עמיתים


The radioluminescence of mixed Ag halide optical fibers (AgClxBr1-x, where 0 < x < 1) is investigated in the range 20-200°C. The main feature in the emission spectrum of the Cl-rich fibers is a broad band centered at 520 nm, which behaves as exp(E/kT), with E ≈0.06 eV. It indicates a competition between nonradiative processes and radiative recombinations of electrons with self-trapped holes. In the Br-rich samples the emission is mainly in the 600-700-nm range and is ascribed to holes trapped at Ag vacancies near divalent and trivalent cationic impurities. An intense new band in the infrared appears in some of the Cl-rich fibers and in all the Br-rich fibers following annealing at 250°C. It is ascribed to the migration of cationic impurities, or of the Ag vacancies that charge compensate them, and to the formation of new complex point defects.

שפה מקוריתאנגלית
עמודים (מ-עד)146-150
מספר עמודים5
כתב עתJournal of the Optical Society of America B: Optical Physics
מספר גיליון2
מזהי עצם דיגיטלי (DOIs)
סטטוס פרסוםפורסם - פבר׳ 1989

טביעת אצבע

להלן מוצגים תחומי המחקר של הפרסום 'Radioluminescence of silver halide optical fibers'. יחד הם יוצרים טביעת אצבע ייחודית.

פורמט ציטוט ביבליוגרפי